PMI foam Core & Sandwich Manufacturer
Polymethyl methacrylamide (PMI) foam is a high-performance closed-cell rigid foam core material copolymerized from methyl acrylate and methacrylonitrile. It exhibits outstanding specific strength, high-temperature resistance, and fatigue resistance, making it widely used in composite sandwich panels for aerospace, marine, rail transportation, and wind turbine blades. Composite Box offers densities ranging from 30 to 300 kg/m³.
Opis produktu
Polymethyl methacrylamide (PMI) foam is a comprehensive high-performance foam core material. With a density range of 30-300 kg/m³, it exhibits excellent tensile and compressive strength, particularly maintaining high mechanical property retention at elevated temperatures.
- Compared to PVC and PET foams, PMI exhibits 30-50% higher strength at equivalent densities and significantly superior heat resistance, withstanding curing temperatures exceeding 180°C in prepreg processes.
- Unlike honeycomb materials, PMI foam is isotropic, facilitating curved surface molding without moisture ingress concerns.
It exhibits balanced shear modulus and compressive strength, delivering outstanding fatigue resistance for sustained dynamic loading. PMI foam also features excellent chemical resistance, low moisture absorption, superior dimensional stability, and a high heat deflection temperature exceeding 200°C.
Get Free Quote of PMI foam Core
Related Products
Fiberglass PMI Sandwich Panel
- Cechy: Lightweight, cost-effective, high impact resistance, strong corrosion resistance, simple forming process
- Zastosowania: Widely used in ship decks, vehicle interiors, radar domes, sports equipment, and building curtain walls. Particularly suitable for curved structural components with medium load requirements, offering excellent cost-performance and durability.
Carbon Fiber/PMI Sandwich Panel
- Cechy: Exceptionally high specific strength, outstanding rigidity, superior fatigue performance, excellent dimensional stability
- Zastosowania: Primarily used in aerospace structural components (e.g., wings, rudders), high-performance racing parts, premium sports equipment, and high-precision instrumentation, meeting the most demanding lightweight and strength requirements.
Fiberglass PMI Sandwich Panel
- Cechy: Superior impact resistance, effective electromagnetic shielding, high stiffness-to-weight ratio, strong environmental resistance
- Zastosowania: Suitable for military vehicle armor, aircraft flooring, electromagnetic shielding compartments, high-speed train interiors, and specialized containers, combining structural strength with specialized functional requirements.
Wymiary
| Size (mm) | Kolor | Density (kg/m³) |
|---|---|---|
| 1000×500 | White | 52 |
| 1250×650 | Beżowy | 75 |
| 2000×1000 | Light Gray | 110 |
| 1500×750 | White | 150 |
| 2500×1250 | Gray | 200 |
Wydajność
| Performance Property | Test Standard | Typical Value (Density 75 kg/m³) | Unit |
|---|---|---|---|
| Wytrzymałość na ściskanie | ASTM D1621 | 2.1 | MPa |
| Wytrzymałość na rozciąganie | ASTM D1623 | 3.2 | MPa |
| Wytrzymałość na ścinanie | ASTM C273 | 1.8 | MPa |
| Wytrzymałość na zginanie | ASTM C393 | 3.5 | MPa |
| Moduł sprężystości | ASTM D1621 | 95 | MPa |
| Heat Deflection Temperature | ASTM D648 | 200 | °C |
| Water Absorption (24h) | ASTM D2842 | <0.5 | % |
Product Parameters:
| Nieruchomość | Value |
|---|---|
| Nazwa | Polyethylene Terephthalate (PET) Rigid Foam |
| Gęstość | 38–200 kg/m³ |
| Grubość | 10–130 mm |
| Przewodność cieplna | 0.03 W/m·K |
| Wytrzymałość na ściskanie | 1.5–2.5 MPa |
| Wytrzymałość na zginanie | 10–15 MPa |
| Water Absorbency | ≤2% |
| Możliwość recyklingu | 100% Recyclable |
| Useful Life | 20 Years |
Generate 4 primary applications
Aerospace: Lightweight structural components such as wings, rudders, radomes, and interior panels
Rail Transportation: High-speed train interior panels, roofs, floors, and sound/heat insulation components
Wind Power Generation: Core reinforcement materials for wind turbine blades to enhance stiffness and fatigue life
Marine Industry: Hulls, decks, and superstructures for luxury yachts and high-speed vessels
Storage Conditions and Precautions
1. Environmental Requirements: Store in a dry, well-ventilated area with relative humidity <70% and temperature between 15-25°C.
2. Avoid Contact: Keep away from organic solvents, strong acids, strong alkalis, and other chemicals to prevent surface corrosion.
3. Protective Measures: Prevent crushing by heavy objects and avoid scratches from sharp items.
4. Stacking Restrictions: Stack flat with a maximum height of 1.5 meters to prevent bottom deformation.
Przetwarzanie niestandardowe
Osadzone konstrukcje wzmacniające
Aby zwiększyć wytrzymałość i funkcjonalność, w panelach kompozytowych można osadzić materiały wzmacniające. Dostępne opcje obejmują sklejkę, profile ze stopu aluminium, rury GRP, stalowe elementy konstrukcyjne i inne.
Przetwarzanie kompozytów wielomateriałowych
Specjalizujemy się w przetwarzaniu materiałów kompozytowych, takich jak FRP, CFRT i rdzenie piankowe, zapewniając doskonałą wydajność przy jednoczesnym spełnieniu różnorodnych wymagań aplikacji.
Precyzyjna obróbka CNC
Zaawansowane centra obróbcze CNC umożliwiają precyzyjne cięcie z dużą prędkością, frezowanie złożonych konturów, wiercenie i nie tylko.
Przetwarzanie krawędziowe
Wykończenie krawędzi i integracja złączy są wykonywane zgodnie z określonymi wymaganiami. Usługi obejmują oklejanie krawędzi, fazowanie i szlifowanie, impregnację wodoodporną i osadzanie nakrętek.
FAQ
Dlaczego warto nas wybrać?
Zadowolenie klienta
Naleganie na wysokiej jakości produkty i serwery, skoncentrowane na doświadczeniu klienta.
Zapewnienie jakości
Ściśle kontrolujemy każdy proces produkcyjny, aby zapewnić naszym klientom niezawodną jakość.
Zaawansowana linia produkcyjna
Najlepsza na świecie linia produkcyjna zapewnia precyzję i wydajność produktu.
Personalizacja
Zapewniamy dostosowanie 100%, dzięki czemu zamówienia są mniej trudne.
English
French
German
Japanese
Korean
Russian
Polish